| Tungsten carbide material specification | |||||
| Grade | Binder (Wt %)Cobalt | Density (g/cm3) | Hardness (HRA) | TRS (>N/mm²) | Grain Size(μm) |
| YG6 | 5.8-6.3 | 14.6-15.0 | 89.5-91 | 1800 | 0.8-2.0 |
| YG6X | 5.8-6.3 | 14.4-14.7 | 90.5-91.5 | 1650 | 0.6-1.0 |
| YG8 | 7.5-8.2 | 14.4-14.7 | 89.0-90.5 | 2200 | 1.0-1.5 |
| YG11 | 11.0-11.5 | 14.2-14.4 | 87.0-88.5 | 2800 | 1.0-2.0 |
| YG11C | 11.0-11.5 | 14.2-14.4 | 86.0-88.0 | 3000 | 1.0-2.5 |
| YG15 | 14.5-15 | 13.9-14.0 | 86.0-88.0 | 3300 | 1.0-2.0 |
| YG20 | 20.0-20.5 | 13.2-13.5 | 84.0-85.0 | 3400 | 1.0-2.0 |
| YG20C | 20.0-20.5 | 13.2-13.5 | 83.0-85.0 | 3600 | 1.0-2.5 |
| K05VF | 4.5-5.0 | 14.6-15.0 | 92.5-93.0 | 1500 | 0.6-1.0 |
| K10VF | 5.5-6.2 | 14.5-14.7 | 91.5-92.5 | 1550 | 0.6-1.0 |
| K20VF | 7.5-8.0 | 14.5-14.7 | 90.5-91.5 | 1800 | 0.6-1.0 |
| Grade | Binder (Wt %)Nickel | Density (g/cm3) | Hardness (HRA) | TRS (>N/mm²) | Grain Size(μm) |
| YN6 | 5.5-6.2 | 14.6-15.0 | 89.5-90.5 | 1800 | 0.8-2.0 |
| YN6X | 5.9-6.5 | 14.5-14.9 | 89.4-91 | 1750 | 0.8-1.8 |
| YN6A | 5.9-6.5 | 14.5-14.8 | 89.5-91.5 | 1850 | 0.8-1.8 |
| YN7 | 6.8-7.2 | 14.4-14.8 | 89.0-90.0 | 1900 | 0.8-1.6 |
| YN8 | 7.8-8.3 | 14.5-14.8 | 89.0-90.0 | 2200 | 0.8-2.0 |
| YN12 | 11.5-12.2 | 14.0-14.4 | 87.5-88.5 | 2600 | 0.8-2.0 |
| YN15 | 14.5-15.2 | 13.7-14.2 | 86.5-88.0 | 2800 | 0.6-1.5 |
Value:
Tungsten Carbide Tread Nozzle is widely used in the blasting industry, and modern development requires increasingly high surface performance of components. Therefore, Carbide Drill Nozzle is an excellent wear component with its fine blasting coating technology and excellent hardness and toughness of tungsten carbide materials.
Highlights:
1. Well handled of surface
2. Satisfactory temperature resistance
3. Strict control in each process
4. Customization product
Advantages:
High speed coating preparation techniques such as explosive coatings can enable materials to have high bonding strength and hardness, as well as low decarburization rate, making them very suitable for Tungsten Carbide Tool Nozzles surface coatings.