Tungsten carbide material specification | |||||
Grade | Binder (Wt %)Cobalt | Density (g/cm3) | Hardness (HRA) | TRS (>N/mm²) | Grain Size(μm) |
YG6 | 5.8-6.3 | 14.6-15.0 | 89.5-91 | 1800 | 0.8-2.0 |
YG6X | 5.8-6.3 | 14.4-14.7 | 90.5-91.5 | 1650 | 0.6-1.0 |
YG8 | 7.5-8.2 | 14.4-14.7 | 89.0-90.5 | 2200 | 1.0-1.5 |
YG11 | 11.0-11.5 | 14.2-14.4 | 87.0-88.5 | 2800 | 1.0-2.0 |
YG11C | 11.0-11.5 | 14.2-14.4 | 86.0-88.0 | 3000 | 1.0-2.5 |
YG15 | 14.5-15 | 13.9-14.0 | 86.0-88.0 | 3300 | 1.0-2.0 |
YG20 | 20.0-20.5 | 13.2-13.5 | 84.0-85.0 | 3400 | 1.0-2.0 |
YG20C | 20.0-20.5 | 13.2-13.5 | 83.0-85.0 | 3600 | 1.0-2.5 |
K05VF | 4.5-5.0 | 14.6-15.0 | 92.5-93.0 | 1500 | 0.6-1.0 |
K10VF | 5.5-6.2 | 14.5-14.7 | 91.5-92.5 | 1550 | 0.6-1.0 |
K20VF | 7.5-8.0 | 14.5-14.7 | 90.5-91.5 | 1800 | 0.6-1.0 |
Grade | Binder (Wt %)Nickel | Density (g/cm3) | Hardness (HRA) | TRS (>N/mm²) | Grain Size(μm) |
YN6 | 5.5-6.2 | 14.6-15.0 | 89.5-90.5 | 1800 | 0.8-2.0 |
YN6X | 5.9-6.5 | 14.5-14.9 | 89.4-91 | 1750 | 0.8-1.8 |
YN6A | 5.9-6.5 | 14.5-14.8 | 89.5-91.5 | 1850 | 0.8-1.8 |
YN7 | 6.8-7.2 | 14.4-14.8 | 89.0-90.0 | 1900 | 0.8-1.6 |
YN8 | 7.8-8.3 | 14.5-14.8 | 89.0-90.0 | 2200 | 0.8-2.0 |
YN12 | 11.5-12.2 | 14.0-14.4 | 87.5-88.5 | 2600 | 0.8-2.0 |
YN15 | 14.5-15.2 | 13.7-14.2 | 86.5-88.0 | 2800 | 0.6-1.5 |
Value:
Carbide Drill Bushingsare mostly used in the oil and natural gas industries for flow control. When selecting a suitableCarbide Bushing Tool. It is necessary to consider factors such as compressive strength and material resistance, in order to ensure the efficient and safe operation of the entire flow control system.
Highlights:
1. Super material for any grades
2. Enhanced temperature resistance
3. Highly great hardness and toughness
4. Easily to be customized
Advantages:
Compared with other companies’ products, our company takes into account specific industry standards when producing Tungsten Carbide Sleeves, providing customers with the best choice. The support of professional technology ensures excellent wear resistance, impact resistance, and corrosion resistance of tungsten carbide shaft sleeves.